| Resin Identification | High light transmittance, low melt flow rate, excellent mechanical properties including surface hardness and temperature resistance, weather resistance, and freely colourable. | |||
| Color | True colours | |||
| Main applications | Suitable for injection moulding, and may also be used for products involving extrusion moulding. | |||
| Processing Method | Injection Molding | |||
| Typical Properties | Test Method | Test Condition | Value | Unit |
| Physical Properties | ||||
| Density | ISO 1183 | 23 ℃ | 1.190 | |
| Shrinkage | ISO 294-4 | 0.2-0.6 | % | |
| Water Absorption Rate | ISO 62 | 24hr | 0.3 | % |
| Physical Properties | ||||
| Refractive index | ISO 489 | nd | 1.490 | |
| Transmi ttance | ISO 13468-1 | 3mm | >93 | % |
| Haze | ISO 14782 | 3mm | 0.9 | % |
| Mechanical Properties | ||||
| Tensile Strength | ISO 527-2 | 5mm/min | 62 | MPa |
| Elongation at Break | 77 | % | ||
| Flexural Strength | ISO 178 | 2mm/min | 142.0 | MPa |
| Flexural Modulus | 3300.0 | kN/m | ||
| Izod Notched Impact Strength | ISO 179-1 | 1.4 | KJ/M2 | |
| Hardness | ISO 2039-2 | M scale | 102.0 | |
| Mdt Index | ISO 1133 | 230℃*3.8kg | 2.0 | g/10min |
| Thermal Performance | ||||
| Heat Deformation Temperature | ISO 75-2 | 1.82 MPa, unannealed | 100.0 | ℃ |
| Coefficient of linear expansion | ISO 11395-2 | 1/℃ | 6*10-5 | ℃ |
| Vika softens | ISO 306 | B/50 | 105.0 | ℃ |
| Flame | ||||
| Flame-retardant properties | UL94 | 1.5mm | HB | |
Note:
(1) Data represents typical values for customer reference only and does not constitute a guarantee of minimum or maximum quality standards or any other purpose.
(2) Performance may vary across different colours.
Caution:
The data and information herein are based on our current knowledge and experience. Should new knowledge or experience arise, modifications to this text's information and data may be made without prior notice. As usage conditions and applicable laws may vary by location and time, it remains the customer's responsibility to determine whether the products and information herein are suitable for their intended use, and to ensure their workplace and product handling methods comply with applicable laws and other governmental regulations. Lisu New Materials assumes no liability or obligation regarding the information in this document and provides no warranties. All implied warranties of merchantability or fitness for a particular purpose are hereby expressly excluded.
| Typical Injection Moulding Process | |
| Plastic Drying | |
| Drying Time | 4–6 hours |
| Drying Temperature | 70–80℃ |
| Drying Equipment | Hot-air dryer |
| Drying Type | Continuous drying (production process) |
| Injection Moulding Process | |
| Nozzle Section | 201-240℃ |
| Plastics Section | 230-270℃ |
| ConveyingSection | 210-240℃ |
| Maximum Injection Temperature | 270℃ |
| Injection Pressure | 40–80MPa |
| Injection Speed | 40–80mm/s |
| Plasticization PressureVelocity | Pressure 65–100MPa, speed 60–85mm/s |
| Plasticization Back Pressure | 20–35MPa |
| Recommended Mould Temperature | 50–70℃ |
Disclaimer: The aforementioned injection moulding processes may vary depending on the product geometry, mould design, and injection moulding machine specifications. Specific adjustments should be made according to actual circumstances.